PROCESSING MATERIALS WITH STAR BURST™
Application examples: micronization of materials for pigments.
Star Burst is the ideal solution for milling and micronization of pigments with minimal contamination. Explore materials by clicking below.
Please note: The magnifications of microscope images before and after processing are not always the same.
Carbon Black - 1
No. of passes: 5
Pressure: 147 MPa
Before: 350 μm

After: 0.2 μm

Carbon Black - 2
No. of passes: 5
Pressure: 78 MPa
Before: 10 μm

After: 0.1 μm

Silk Powder
No. of passes: 3
Pressure: 196 MPa
Before: 8 μm

After: 1 μm

Aluminum Hydroxide
No. of passes: 10
Pressure: 147 MPa
Before: 33 μm

After: 2.5 μm

Blue Pigment
No. of passes: 10
Pressure: 147 MPa
Before: 10 μm

After: 0.1 μm

White Pigment
No. of passes: 10
Pressure: 245 MPa
Before: 15 μm

After: 0.8 μm

Green Pigment
No. of passes: 10
Pressure: 196 MPa
Before: 3 μm

After: 0.1 μm